Coated article with low-E coating including IR reflecting layers(s) and corresponding method

ABSTRACT

A coated article is provided with a low-emissivity (low-E) layer stack for use in a window unit or the like. The layer stack, or coating, may permit the coated article to achieve one or more of a fairly low solar factor (SF) value, a high selectivity (T vis /SF) value, substantially neutral color at normal and/or off-axis viewing angles, and/or low emissivity. When high selectivity values are achieved, there is provided a high ratio of visible transmission to SF, which is a desirable feature in certain example instances. In certain example embodiments, a sub-oxide layer (e.g., NiCrO x ) may be used as a contact layer under an infrared (IR) reflecting layer in order to permit low SF values, high selectivity, and good coloration to be achieved.

This is a Continuation-in-Part (CIP) of U.S. patent application Ser. No. 10/931,212, filed Sep. 1, 2004, the disclosure of which is hereby incorporated herein by reference.

This invention relates to a coated article including a low-E coating, and/or methods of making the same. Coated articles according to certain example embodiments of this invention may be used in the context of insulating glass (IG) window units, other types of windows, or in any other suitable application.

BACKGROUND OF THE INVENTION

Coated articles are known in the art for use in window application such as insulating glass (IG) window units, vehicle windows, and/or the like. In certain situations, designers of coated articles often strive for a combination of high visible transmission, substantially neutral color, low emissivity (or emittance), and blockage of undesirable radiation such as infrared (IR) radiation to prevent undesirable heating of a building interior or the like. High visible transmission for example may permit coated articles to be more desirable in certain window applications, whereas low-emissivity (low-E), low SHGC (solar heat gain coefficient), and low SF (solar factor, or g-value) characteristics permit coated articles to block significant amounts of undesirable radiation so as to reduce, for example, undesirable heating of vehicle or building interiors.

Solar factor (SF, or g-value), calculated in accordance with DIN standard 67507, relates to a ratio between the total energy entering a room or the like through a glazing and the incident solar energy. Thus, it will be appreciated that low SF values are indicative of good solar protection against undesirable heating of rooms or the like protected by windows/glazings. For example, a low SF value is indicative of a coated article (e.g., IG unit such as a double glazing) that is capable of keeping a room fairly cool in summertime months during hot ambient conditions.

While low SF values are typically desirable for coated articles such as IG window units, the achievement of low SF values typically comes at the expense of visible transmission and/or coloration. It is often desirable, but very difficult, to achieve a combination of a high visible transmission and a low SF value for a coated article such as an IG window unit or the like. In this regard, the ratio between visible transmission (T_(vis)) and SF is sometimes referred to as “selectivity.” In other words, the “selectivity” of a coated article is defined by T_(vis)/SF.

High selectivity (T_(vis)/SF) values are indicative of a combination of high visible transmission and low SF, and are thus often desirable. Unfortunately, high selectivity (T_(vis)/SF) values have heretofore been difficult to achieve.

For example, an object of glazings described in U.S. Pat. No. 6,673,427 to Guiselin is to achieve the “highest possible” selectivity (i.e., T_(vis)/SF). In this regard, see the '427 patent at column 1, lines 54-60. Given this goal of achieving the highest possible selectivity (i.e., T_(vis)/SF), glazings according to the '427 patent were only able to achieve a selectivity of about 1.6 to 1.7 in a double glazing (see the '427 patent at column 7, lines 3-5). In particular, Example 3 of the '427 patent achieved a selectivity of about 1.67 whereas Example 4 of the '427 patent achieved a selectivity of about 1.61 as evidenced by Table 2 of the '427 patent (e.g., for Example 4, 61/38=1.605).

While higher selectivities are sometimes achievable, they have come at the expense of the requirement for excess IR reflecting layers and/or undesirable coloration at normal and/or off-normal viewing angles such as 45 degrees. For example, Examples 1 and 2 of U.S. Pat. No. 5,595,825 to Guiselin used triple-silver coatings to allegedly achieve selectivity values in double glazings of 1.97 and 1.82, respectively. However, the coatings of the '825 patent required the use of three separate silver layers at particular thicknesses to achieve such selectivity values. In certain example instances, the requirement of three separate silver layers (IR reflecting layers) may be undesirable in that such coatings are more costly and burdensome to manufacture and may be more susceptible to yield problems. Furthermore, it is unclear from the '825 patent whether the coatings thereof realize significant color shifts upon change in viewing angle and/or undesirable coloration.

U.S. 2003/0150711 to Laird, the disclosure of which is hereby incorporated herein by reference, discloses a coating having the following layers oriented from the glass substrate outwardly: Glass Substrate Thickness (Å) TiO₂ 200 ZnO 90 Ag 130 NiCrO_(x) 30 SnO₂ 680 ZnO 90 Ag 168 NiCrO_(x) 30 SnO₂ 125 Si₃N₄ 220

While the aforesaid coated article of U.S. 2003/0150711 achieves excellent results in many respects, when used in the context of an IG window unit (or double glazing), it typically achieves a selectivity (T_(vis)/SF) of about 1.7 or so. Higher selectivity values are often desirable.

In view of the above, it will be apparent to those skilled in the art that there exists a need for coated articles which are capable of providing one or more of high selectivity values, low SF values, substantially neutral color at normal and/or off-axis viewing angles, and/or low emissivity (or emittance).

BRIEF SUMMARY OF EXAMPLE EMBODIMENTS OF THE INVENTION

In certain example embodiments of this invention, a coated article is provided with a layer stack which may permit the coated article to achieve one or more of high selectivity values, fairly low solar factor (SF) values, substantially neutral color at normal and/or off-axis viewing angles, and/or low emissivity. When high selectivity (T_(vis)/SF) values are achieved, there is provided a high ratio of visible transmission to solar factor (SF), which will be appreciated by those skilled in the art. Coated articles according to certain example embodiments of this invention may be, or may be used in, IG window units, monolithic windows, or other types of windows.

In certain example embodiments of this invention, a coated article is provided which has both high selectivity and desirable coloration at both normal and off-axis viewing angles such as 45 degrees from normal. Moreover, in certain example embodiments, the coloration of the coated article does not shift by more than a predetermined amount between a normal viewing angle and an off-axis viewing angle of 45 degrees for example.

In certain example embodiments of this invention, a coated article such as an IG window unit realizes a selectivity value (T_(vis)/SF) of at least 1.75, more preferably of at least 1.80, even more preferably of at least 1.85, and sometimes at least 1.90.

In certain example embodiments of this invention, high selectivity is achieved without the need for more than two infrared (IR) reflecting layers (e.g., silver layers). Moreover, fairly low SF values are achieved in certain example embodiments of this invention. In certain example embodiments of this invention, coated articles realize a high selectivity value, in combination with a SF value of no greater than 35.0, more preferably a SF value of no greater than 34.0, even more preferably a SF value of no greater than 33.0, and most preferably a SF value of no greater than 32.5. This permits coated articles, for example, to realize good selectivity while at the same time blocking significant undesirable radiation from reaching a building interior or the like.

In certain example embodiments of this invention, coated articles realize a visible transmission of from about 50 to 70%, more preferably from about 55 to 65%, and most preferably from about 58 to 64% in a monolithic and/or IG unit context.

In certain example embodiments of this invention, the low-E coating of a coated article includes only two IR reflecting layers (e.g., only two silver or silver-based layers). While other numbers of IR reflecting layers may sometimes be provided, the use of two is preferable in certain instances in that more such layers are not required thereby making coatings easier and cost effective to manufacture and less susceptible to yield problems.

In certain example embodiments of this invention, a coated article is provided with an infrared (IR) reflecting layer(s) of or including a material such as silver (Ag), gold, or the like. The IR reflecting layer is located between respective lower and upper contact layers, each of which contacts the IR reflecting layer. The contact layers may be made of material(s) such as an oxide of nickel-chrome (NiCrO_(x)) in certain example embodiments of this invention. In certain embodiments, the lower contact layer is of the sub-oxide type, whereas the upper contact layer is more oxided than is the lower contact layer. Surprisingly and unexpectedly, it has been found that by using a sub-oxide contact layer under and contacting the IR reflecting layer and a more oxided contact layer over the IR reflecting layer, significantly higher selectivity values and lower SF values may be achieved in combination with desirable coloration at normal and/or off-axis viewing angles. These represent significant example advantages in the art.

In certain example embodiments of this invention, there is provided a insulating glass (IG) window unit comprising first and second glass substrates, and a coating supported by one of the substrates, the coating comprising: first and second infrared (IR) reflecting layers comprising silver provided between at least a pair of dielectric layers, so that the coating has only two IR reflecting layers; at least one of the IR reflecting layers comprising silver being sandwiched between and contacting first and second contact layers, each of said first and second contact layers comprising an oxide, wherein the first contact layer is located below said IR reflecting layer and is oxided to a lesser extent than is the second contact layer located above said IR reflecting layer; and wherein the IG window unit has a visible transmission of from about 50 to 70%, a selectivity (T_(vis)/SF) of at least 1.75, and a solar factor (SF) of no greater than 35.0.

In other example embodiments of this invention, there is provided a coated article including a coating supported by a glass substrate, the coating comprising at least one layer comprising silver sandwiched between and contacting first and second oxided contact layers, wherein the first contact layer is located below said layer comprising silver and is oxided to a lesser extent than is the second contact layer located above said layer comprising silver; and wherein the coated article has a selectivity (T_(vis)/SF) of at least 1.75.

In still further example embodiments of this invention, there is provided an insulating glass (IG) window unit comprising: first and second glass substrates, and a coating supported by one of the substrates, the coating comprising first and second infrared (IR) reflecting layers, and no further IR reflecting layer(s), each of the first and second IR reflecting layers being sandwiched between and contacting a pair of contact layers, wherein the IG window unit has a selectivity (T_(vis)/SF) of at least 1.75, and a solar factor (SF) of no greater than 34.0.

BRIEF DESCRIPTION OF THE DRAWINGS

FIG. 1 is a cross sectional view of a coated article according to an example embodiment of this invention.

FIG. 2 is a cross section view of an IG unit according to an example embodiment of this invention.

DETAILED DESCRIPTION OF EXAMPLES OF THE INVENTION

Referring now more particularly to the accompanying drawings in which like reference numerals indicate like parts throughout the several views.

Coated articles herein may be used in applications such as IG window units (which may include two or more glass substrates with a space therebetween), monolithic windows, and/or any other suitable application that includes single or multiple glass substrates for a window or the like. In certain example embodiments of this invention, the coating includes a double-silver stack (i.e., two layers each of which comprises or is composed of silver), although this invention is not so limited in all instances.

In certain example embodiments of this invention, a coated article is provided with a layer stack which may permit the coated article to achieve one or more of high selectivity (T_(vis)/SF), a fairly low solar factor (SF), substantially neutral color at normal and/or off-axis viewing angles, and/or low emissivity. One, two, three, or all of these features may be achieved in different embodiments of this invention. When high selectivity (T_(vis)/SF) is achieved, there is provided a high ratio of visible transmission (T_(vis)) to solar factor (SF), which will be appreciated by those skilled in the art as being an indication of a combination of good visible transmission and good solar protection of a building and/or vehicle interior for example.

In certain example embodiments of this invention, a coated article such as an IG window unit (e.g., with two spaced apart glass substrates) realizes a high selectivity (T_(vis)/SF) of at least 1.75, more preferably of at least 1.80, even more preferably of at least 1.85, and sometimes at least 1.90. In certain example embodiments of this invention, coated articles realize a high selectivity value, in combination with a SF of no greater than 35.0, and more preferably a SF of no greater than 34.0, even more preferably a SF of no greater than 33.0, and most preferably a SF of no greater than 32.5 (SF, or g-value, is calculated in accordance with DIN 67507, the disclosure of which is hereby incorporated herein by reference). This permits coated articles, for example, to realize good selectivity while at the same time blocking significant undesirable radiation from reaching a building interior or the like.

In certain example embodiments of this invention, a coated article is provided which has both high selectivity and desirable coloration at both normal and off-axis viewing angles such as 45 degrees from normal. Moreover, in certain example embodiments, the coloration of the coated article does not shift by more than a predetermined amount between a normal viewing angle and an off-axis viewing angle of 45 degrees for example.

In certain example embodiments of this invention, coated articles realize a visible transmission of from about 50 to 70%, more preferably from about 55 to 65%, and most preferably from about 58 to 64% in a monolithic and/or IG unit context.

Sheet resistance (R_(s)) is indicative of emissivity or emittance. Low sheet resistance is achieved in certain example embodiments of this invention. In certain example embodiments of this invention, a coated articles realizes a sheet resistance (R_(s)) of no greater than about 3.0 ohms/square, more preferably no greater than about 2.0 ohms/square, and most preferably no greater than about 1.9 ohms/square before any optional heat treatment such as tempering. Such low sheet resistance values are indicative of low emissivity.

In certain example embodiments of this invention, the low-E coating of a coated article includes only two IR reflecting layers (e.g., only two silver or silver-based layers). While other numbers of IR reflecting layers may sometimes be provided, the use of two is preferable in certain instances in that low-emittance can be achieved and more such layers are not required thereby making coatings easier and cost effective to manufacture and less susceptible to yield problems.

In certain example embodiments of this invention, an IR reflecting layer is located between respective lower and upper contact layers, each of which contacts the IR reflecting layer. The contact layers may be made of material(s) such as an oxide of nickel-chrome (NiCrO_(x)) in certain example embodiments of this invention. In certain embodiments, the lower contact layer is of the sub-oxide type, whereas the upper contact layer is more oxided than is the lower contact layer. Surprisingly and unexpectedly, it has been found that by using a sub-oxide contact layer under and contacting the IR reflecting layer and a more oxided contact layer over the IR reflecting layer, significantly higher selectivity values and lower SF values may be achieved in combination with desirable coloration at normal and/or off-axis viewing angles. These represent significant example advantages in the art.

FIG. 1 is a side cross sectional view of a coated article according to an example non-limiting embodiment of this invention. The coated article includes substrate 1 (e.g., clear, green, bronze, or blue-green glass substrate from about 1.0 to 10.0 mm thick, more preferably from about 1.0 mm to 7.0 mm thick), and coating (or layer system) 30 provided on the substrate 1 either directly or indirectly. The coating (or layer system) 30 includes: dielectric titanium oxide layer 3 which may be TiO_(x) (e.g., where x is from 1.5 to 2.0), first lower contact layer 7 (which contacts IR reflecting layer 9), first conductive and preferably metallic infrared (IR) reflecting layer 9, first upper contact layer 11 (which contacts layer 9), dielectric layer 13 (which may be deposited in one or multiple steps in different embodiments of this invention), dielectric layer 15 which supports contact layer 17 and may be of or include zinc oxide, second lower contact layer 17 (which contacts IR reflecting layer 19), second conductive and preferably metallic IR reflecting layer 19, second upper contact layer 21 (which contacts layer 19), dielectric layer 23, and finally protective dielectric layer 25. The “contact” layers 7, 11, 17 and 21 each contact at least one IR reflecting layer (e.g., layer based on Ag, Au or the like). The aforesaid layers 3-25 make up low-E coating 30 which is provided on glass or plastic substrate 1.

In monolithic instances, the coated article includes only one glass substrate 1 as illustrated in FIG. 1. However, monolithic coated articles herein may be used in devices such as IG window units, or the like. As for IG window units, an IG window unit may include two or more spaced apart glass or plastic substrates. An example IG window unit is illustrated and described, for example, in U.S. Pat. No. 6,632,491, the disclosure of which is hereby incorporated herein by reference. An example IG window unit is also shown in FIG. 2 and may include, for example, the coated glass substrate 1 shown in FIG. 1 coupled to another glass substrate 2 via spacer(s), sealant(s) or the like 4 with a gap 6 being defined therebetween. This gap 6 between the substrates in IG unit embodiments may in certain instances be filled with a gas such as argon (Ar). The gap 6 may or may not be at a pressure less than atmospheric in different embodiments of this invention.

Still referring to FIG. 2, an example IG unit may comprise a pair of spaced apart glass substrates (1 and 2) each about 6 mm thick one of which is coated with a coating 30 herein in certain example instances, where the gap 6 between the substrates may be from about 5 to 30 mm, more preferably from about 10 to 20 mm, and most preferably about 16 mm. In certain example embodiments, the coating 30 is provided on the interior surface of the outer glass substrate 1 as shown in FIG. 2 (i.e., on surface #2 from the outside), although it may be provided on the other substrate 2 in alternative embodiments of this invention.

Dielectric layer 3 may be of or include titanium oxide in certain example embodiments of this invention. This layer is provided for anti-reflective purposes, and preferably has an index of refraction (n) of from about 2.0 to 2.6, more preferably from about 2.2 to 2.5. Layer 3 may be provided in direct contact with the glass substrate 1 in certain example embodiments of this invention, or alternatively other layer(s) may be provided between the substrate 1 and layer 3 in certain instances.

Infrared (IR) reflecting layers 9 and 19 are preferably substantially or entirely metallic and/or conductive, and may comprise or consist essentially of silver (Ag), gold, or any other suitable IR reflecting material. IR reflecting layers 9 and 19 help allow the coating to have low-E and/or good solar control characteristics. The IR reflecting layers 9 and/or 19 may, however, be slightly oxidized in certain embodiments of this invention.

Contact layers 11, 17 and 21 may be of or include nickel (Ni) oxide, chromium/chrome (Cr) oxide, or a nickel alloy oxide such as nickel chrome oxide (NiCrO_(x)), or other suitable material(s), in certain example embodiments of this invention. The use of, for example, NiCrO_(x) in these layers (11, 17 and/or 21) allows durability to be improved. These contact layers may or may not be continuous in different embodiments of this invention across the entire IR reflecting layer.

In certain example embodiments of this invention, the upper contact layers 11 and/or 21 that are located above the respective IR reflecting layers 9 and 19 are deposited in a manner so as to be oxided to a first extent. In certain example embodiments, the upper contact layers 11 and/or 21 may be substantially fully oxided.

Surprisingly, it has been found that by using a sub-oxide contact layer 17 under and contacting the IR reflecting layer 19 and a more oxided contact layer 21 over the IR reflecting layer 19, significantly higher selectivity values and lower SF values can be achieved in combination with desirable coloration at normal and/or off-axis viewing angles. These represent significant example advantages in the art. In particular, it has been found that such unexpected results can be achieved when the contact layer 17 under the IR reflecting layer 19 is deposited in a manner so as to be oxided to a lesser extent than upper contact layer 21 on the other side of the IR reflecting layer 19. In certain example embodiments, contact layers 17 and 21 may be composed of oxides of the same metal(s), yet be oxided to different extents where the lower contact layer 17 is oxided to a lesser extent than is the upper contact layer 21. For example, in certain example embodiments of this invention, lower NiCrO_(x) contact layer 17 is a sub-oxide (i.e., only partially oxided) whereas upper NiCrO_(x) contact layer 21 is substantially fully oxided as deposited by sputtering or the like.

In certain example embodiments of this invention, as deposited and/or in the final product which is not thermally tempered in certain embodiments, sub-oxide contact layer 17 may have no more than about 80% of the oxygen content of the upper contact layer 21, more preferably no more than about 70% of the oxygen content of the upper contact layer 21, and most preferably no more than about 60% of the oxygen content of the upper contact layer 21. In each of these cases, as well as others, it will be appreciated that the lower contact layer 17 under the IR reflecting layer 19 is oxided to a lesser extent than is the upper contact layer 21 located over the IR reflecting layer 19 in at least certain portions of the respective contact layers.

In order to deposit sub-oxide contact layer 17 in a manner so as to be less oxided than upper contact layer 21, even when they are oxides of the same metal(s) such as Ni and/or Cr, less oxygen gas flow per kW of sputtering power may be used in sputtering layer 17 compared to layer 21. For example, given similar or the same type of sputtering target(s) (e.g., using NiCr based targets for each layer), an oxygen gas flow of about 5 ml/kW may be used when sputtering sub-oxide lower contact layer 17, whereas an oxygen gas flow of about 10 ml/kW may be used when sputtering substantially fully oxided upper contact layer 21 (the remainder of the gas flows may be made up of Ar or the like). In this particular example, the oxygen gas flow per kW of sputtering power for sub-oxide layer 17 is about 50% of that for the more oxided upper contact layer 21. In certain example embodiments of this invention, the oxygen gas flow per kW of sputtering power for sub-oxide layer 17 is no more than about 80% of that used for the upper more oxided contact layer 21, more preferably no more than about 70% of that used for the upper more oxided contact layer 21, and even more preferably no more than about 60% of that used for the upper more oxided contact layer 21.

In certain example embodiments of this invention, the upper contact layers 11 and 21 provided over the respective IR reflecting layers may be deposited in similar or the same manners.

Lower contact layer 7 and/or dielectric layer 15 in certain embodiments of this invention are of or include zinc oxide (e.g., ZnO). The zinc oxide of layer(s) 7, 15 may contain other materials as well such as Al (e.g., to form ZnAlO_(x)). For example, in certain example embodiments of this invention, one or more of zinc oxide layers 7, 15 may be doped with from about 1 to 10% Al, more preferably from about 1 to 5% Al, and most preferably about 2 to 4% Al. The use of zinc oxide 7 under the silver 9 allows for an excellent quality of silver to be achieved.

Dielectric layer 13 may be of or include tin oxide in certain example embodiments of this invention. However, as with other layers herein, other materials may be used in different instances. Dielectric layer 23 may be of or include tin oxide in certain example embodiments of this invention. However, layer 23 is optional and need not be provided in certain example embodiments of this invention. Dielectric layer 25, which may be an overcoat including one or more layers in certain example instances, may be of or include silicon nitride (e.g., Si₃N₄) or any other suitable material in certain example embodiments of this invention. Optionally, other layers may be provided above layer 25. For example, an overcoat layer of or including zirconium oxide (not shown) may be formed directly on top of the silicon nitride layer 25 in certain example embodiments of this invention. Silicon nitride layer 25 may be doped with Al or the like in certain example embodiments of this invention.

Other layer(s) below or above the illustrated coating may also be provided. Thus, while the layer system or coating is “on” or “supported by” substrate 1 (directly or indirectly), other layer(s) may be provided therebetween. Thus, for example, the coating of FIG. 1 may be considered “on” and “supported by” the substrate 1 even if other layer(s) are provided between layer 3 and substrate 1. Moreover, certain layers of the illustrated coating may be removed in certain embodiments, while others may be added between the various layers or the various layer(s) may be split with other layer(s) added between the split sections in other embodiments of this invention without departing from the overall spirit of certain embodiments of this invention. Thus, the use of the word “on” herein is not limited to being in direct contact with.

While various thicknesses and materials may be used in layers in different embodiments of this invention, example thicknesses and materials for the respective layers on the glass substrate 1 in the FIG. 1 embodiment are as follows, from the glass substrate outwardly (the silver thicknesses are approximations based on deposition data): Example Materials/Thicknesses; Fig. 1 Embodiment Preferred Layer Range (Å) More Preferred (Å) Example (Å) Glass (1-10 mm thick) TiO_(x) (layer 3)  10-450 Å  50-250 Å  88 Å ZnO_(x) (layer 7)  10-300 Å  40-150 Å 141 Å Ag (layer 9)  50-250 Å  60-120 Å  70 Å NiCrO_(x) (layer 11)  10-100 Å 30-45 Å  38 Å SnO₂ (layer 13)    0-1,000 Å 350-850 Å 684 Å ZnO_(x) (layer 15)  10-300 Å  40-150 Å 122 Å NiCrO_(x) (layer 17)  10-100 Å 25-50 Å  24 Å Ag (layer 19)  50-250 Å  80-220 Å 205 Å NiCrO_(x) (layer 21)  10-100 Å 30-55 Å  42 Å SnO₂ (layer 23)  0-750 Å 150-300 Å 138 Å Si₃N₄ (layer 25)  0-750 Å 100-320 Å 203 Å

In the Example (see right-hand column above for thickneses in the Example), the NiCrO_(x) contact layers 11 and 21 located above the respective IR reflecting layers were substantially fully oxided, whereas the NiCrO_(x) contact layer 17 under the top IR reflecting layer 19 was a sub-oxide and thus oxided to a lesser extent than the other NiCrO_(x) contact layers. As explained herein, this has unexpectedly permitted certain optical advantages to be achieved.

In certain example embodiments of this invention, coated articles herein may have the following optical and solar characteristics when provided in the context of an IG unit. The optics may be measured in accordance with Ill. C, 2 degree observer as is known in the art. In certain embodiments, at least the coated glass substrate is not thermally tempered. An example IG Unit, for purposes of reference only, includes a pair of 6 mm glass substrates (clear and/or green colored) separated by a space of 16 mm, not thermally tempered. The below data was taken at the normal viewing angle, unless otherwise specified (e.g., the ΔR_(g)Y data, Δa*_(g) data (absolute value), and Δb*_(g) data (absolute value) are indicative in the change in the listed value between the 0 degree viewing angle and a 45 degree viewing angle):

Example Optical Characteristics (IG Unit)

More Characteristic General Preferred Best Selectivity (T_(vis)/SF): ≧1.75 ≧1.80 ≧1.85 (or ≧1.90) SF (DIN 67507): ≦35.0 34.0 ≦33.0 (or ≦32.5) SHGC: ≦35.0 ≦34.0 ≦33.0 T_(vis) (or TY)(III C, 2 deg.): 50-70% 55-65% 58-64% a*_(t): −8 to +2 31 6 to +1 −5.5 to 0 b*_(t): −2 to +8 −1 to +5 0 to +4 R_(g)Y (outside refl.): ≦17% ≦16% ≦15% a*_(g): −5 to +2 −3.5 to +2 −3.0 to +1 b*_(g): −15 to +10 −12.0 to +4 −10 to 0 R_(g)Y (45° VA): ≦17% ≦16% ≦15% a*_(g): −5 to +3 −3 to +2 −2.5 to +2 b*_(g): −15 to +10 −13.0 to +4 −12 to 0 ΔR_(g)Y (shift from 0-45°): ≦1.5% ≦1.0% ≦0.5% Δa*_(g): ≦3.5 ≦2.5 ≦2.1 Δb*_(g): ≦3.5 ≦2.0 ≦1.5 R_(s) (ohms/square): ≦3.0 ≦2.0 ≦1.9

In certain example embodiments of this invention, coated articles herein may have the following optical and solar characteristics when measured monolithically (e.g., clear glass substrate 6 mm thick, not thermally tempered).

Example Optical Characteristics (Monolithic)

More Characteristic General Preferred Best T_(vis) (or TY)(III C, 2 deg.): 55-75% 60-70% 62-69% a*_(t): −8 to +2 −6 to +1 −5 to 0 b*_(t): −2 to +8 −1 to +5 0 to +4 R_(g)Y (glass side refl.): ≦16% ≦14% ≦13% a*_(g): −5 to +2 −3 to +2 −2 to 0 b*_(g): −20 to +10 −15 to +3 −13 to 0 ΔR_(g)Y (shift from 0-45°): ≦1.5% ≦1.0% ≦0.5% Δa*_(g): ≦3.5 ≦2.5 ≦1.0 Δb*_(g): ≦3.5 ≦2.5 ≦2.0 R_(f)Y (film side refl.): ≦21% ≦16% ≦14% a*_(f): −5 to +6 −3 to +4 −2 to +3 b*_(f): −20 to +25 −15 to +20 −10 to +15 R_(s) (ohms/square): ≦3.0 ≦2.0 ≦1.9

The following examples are provided for purposes of example only, and are not intended to be limiting unless specifically claimed.

EXAMPLE

The following Example 1 was made via sputtering the coating shown in FIG. 1 on a 6 mm thick clear glass substrates 1 so as to have approximately the layer stack set forth below and shown in FIG. 1. The physical layer thicknesses are approximations, and are in units of angstroms (Å).

Layer Stack for Example 1

Layer Glass Substrate Thickness (Å) TiO₂ 88 ZnAlO_(x) 141 Ag 70 NiCrO_(x) (sco) 38 SnO₂ 684 ZnAlO_(x) 122 NiCrO_(x) 24 (sub-oxide) Ag 205 NiCrO_(x) (sco) 42 SnO₂ 138 Si₃N₄ 203

In the Example above, the NiCrO_(x) contact layer 17 under the top IR reflecting layer 19 was a sub-oxide, whereas the other two NiCrO_(x) contact layers were substantially fully oxided (“sco” stands for substantially completely oxided). The Example coated article was not thermally tempered or heat bent. The NiCrO_(x) contact layer 17 under the top IR reflecting layer 19 was sputter-deposited as a sub-oxide by using an oxygen gas flow in the sputtering chamber (with a NiCr sputtering target) of about 7.5 ml/kW, whereas the other two NiCrO_(x) contact layers 11 and 21 were sputter-deposited in substantially fully oxided form by using an oxygen gas flow in the respective sputtering chambers of about 9.5 to 11.3 ml/kW (where kW is indicative of the power used as is known in the art). Thus, the sub-oxide contact layer 17 was oxided to a lesser extent than were contact layers 11 and 21 and was thus more absorbing.

The coated article of Example 1, in monolithic form, had the following characteristics (Ill. C, 2 deg. for visible transmission and reflectance at normal viewing angles).

Example 1 (Monolithic)

Characteristic Example 1 Visible Trans. (T_(vis) or TY): 67.23% a* −4.68 b* 3.74 Glass Side Reflectance (RY): 12.05% a* −1.14 b* −10.93 Glass Side Reflectance (RY) (45° VA): about 11.6% a* about −2 b* about −9.3 Film Side Reflective (FY): 12.01% a* 2.31 b* 11.83 R_(s) (ohms/square): 1.8

It can be seen from the above that the glass side reflectance changed very little even when the viewing angle (VA) was shifted from 0 to 45 degrees (or a similar shift in incident light). Thus, the coated article is advantageous in that it looks similar at many different viewing angles.

The coated article of Example 1 was then coupled to another glass substrate about 6 mm thick to form an IG window unit as shown in FIG. 2, without being tempered. The gap between the two glass substrates was about 16 mm thick. The IG unit had the following characteristics, and a colour rendering index of 95.

Example 1 (IG Unit)

Characteristic Example 1 Selectivity (T_(vis)/SF): 1.91 SF: 32.3 Visible Trans. (t_(vis) or TY): 61.6% a* −4.92 b* 3.54 Glass Side/Outside Reflectance (RY): 15% a* −2.51 b* −8.28 R_(s) (ohms/square): 1.8

Moreover, it was surprisingly found that the reflective/outside color is substantially independent of the polarization state of the incident light. In other words, the reflective/outside color does not significantly change as a function of the polarization state of the incident light. This represents a significant improvement in the art.

It can be seen from the Example set forth above that a combination of high selectivity and fairly low SF was achieved in both examples, using only two IR reflecting layers, representing a significant example advantage in the art.

In the parent case, a Comparative Example (CE) coated article was made similar to Example 1 in the parent, except that in the CE the contact layer 17 was not present. The result in the CE was an IG unit with a higher SF and higher selectivity. Thus, it can be seen that the use of a contact layer 17 in sub-oxide form surprisingly and unexpectedly results in a coated article having an improved SF value as well as improved selectivity.

While the invention has been described in connection with what is presently considered to be the most practical and preferred embodiment, it is to be understood that the invention is not to be limited to the disclosed embodiment, but on the contrary, is intended to cover various modifications and equivalent arrangements included within the spirit and scope of the appended claims. 

1. An insulating glass (IG) window unit comprising: first and second glass substrates, and a coating supported by one of the substrates, the coating comprising: first and second infrared (IR) reflecting layers comprising silver provided between at least a pair of dielectric layers, so that the coating has only two IR reflecting layers; at least one of the IR reflecting layers comprising silver being sandwiched between and contacting first and second contact layers, each of said first and second contact layers comprising an oxide, wherein the first contact layer is located below said IR reflecting layer and is oxided to a lesser extent than is the second contact layer located above said IR reflecting layer; and wherein the IG window unit has a visible transmission of from about 50 to 70%, a selectivity (T_(vis)/SF) of at least 1.75, and a solar factor (SF) of no greater than 35.0.
 2. The IG window unit of claim 1, wherein the first contact layer comprises an oxide of Ni and/or Cr.
 3. The IG window unit of claim 1, wherein each of the first and second contact layers comprise an oxide of Ni and/or Cr.
 4. The IG window unit of claim 1, wherein said one IR reflecting layer comprising silver that is sandwiched between and contacting the first and second contact layers is located above the other IR reflecting layer comprising silver.
 5. The IG window unit of claim 1, wherein each of the first and second contact layers comprise an oxide of NiCr.
 6. The IG window unit of claim 1, wherein the IG window unit has a selectivity of at least 1.80.
 7. The IG window unit of claim 1, wherein the IG window unit has a selectivity of at least 1.85.
 8. The IG window unit of claim 1, wherein the IG window unit has a selectivity of at least 1.90.
 9. The IG window unit of claim 1, wherein the IG window unit has an outside reflective a* value, at a normal viewing angle, of from −3.5 to +2.
 10. The IG window unit of claim 1, wherein the IG window unit has an outside reflective a* value, at a normal viewing angle, of from −3 to +1.
 11. The IG window unit of claim 1, wherein the coating has a sheet resistance (R_(s)) of no greater than 3.0 ohms/square.
 12. The IG window unit of claim 1, wherein the coating has a sheet resistance (R_(s)) of no greater than 2.0 ohms/square.
 13. The IG window unit of claim 1, wherein the glass substrate supporting the coating is not heat treated with the coating thereon.
 14. The IG window unit of claim 1, wherein the IG window unit has a visible transmission of from about 55 to 655%.
 15. The IG window unit of claim 1, wherein the IG unit has an outside a* value which does not change by more than 3.5 given a viewing angle shift from 0 to 45 degrees.
 16. The IG window unit of claim 1, wherein the IG unit has an outside a* value which does not change by more than 2.5 given a viewing angle shift from 0 to 45 degrees.
 17. The IG window unit of claim 1, wherein outside reflective a* and b* of the IG window unit do not change by more than 3.5 given a viewing angle shift from 0 to 45 degrees.
 18. The IG window unit of claim 1, wherein the coating comprises at least the following layers from the substrate which supports the coating outwardly: a first dielectric layer; a layer comprising zinc oxide; the first IR reflecting layer comprising silver; a contact layer comprising an oxide of Ni and/or Cr; a second dielectric layer; another layer comprising zinc oxide; said first contact layer; said second IR reflecting layer comprising silver; said second contact layer; a third dielectric layer; and an overcoat layer.
 19. An insulating glass (IG) window unit comprising: first and second glass substrates, and a coating supported by one of the substrates, the coating comprising: first and second infrared (IR) reflecting layers, and no further IR reflecting layer(s), each of the first and second IR reflecting layers being sandwiched between and contacting a pair of contact layers, wherein the IG window unit has a selectivity (T_(vis)/SF) of at least 1.75, and a solar factor (SF) of no greater than 34.0.
 20. The IG window unit of claim 19, wherein at least one of the contact layers comprises an oxide of Ni and/or Cr.
 21. The IG window unit of claim 19, wherein each of the IR reflecting layers comprise silver.
 22. The IG window unit of claim 19, wherein the IG window unit has a SF of no greater than 33.0.
 23. The IG window unit of claim 19, wherein the contact layer under at least one of the IR reflecting layers is oxided to a lesser extent than is the contact layer located over and contacting that IR reflecting.
 24. The IG window unit of claim 19, wherein the second IR reflecting layer is located above the first IR reflecting layer, and wherein the contact layer under the first IR reflecting layer comprises zinc oxide and the contact layer under the second IR reflecting layer comprises an oxide of Ni and/or Cr.
 25. The IG window unit of claim 19, wherein the IG window unit has a selectivity of at least 1.80.
 26. The IG window unit of claim 19, wherein the IG window unit has a selectivity of at least 1.85.
 27. The IG window unit of claim 19, wherein the IG window unit has a selectivity of at least 1.90 and a SF of no greater than 33.0.
 28. The IG window unit of claim 19, wherein the IG window unit has a visible transmission of from 50 to 70%.
 29. The IG window unit of claim 19, wherein the IG window unit has an outside reflective a* value, at a normal viewing angle, of from −3.5 to +2.
 30. The IG window unit of claim 19, wherein the IG window unit has an outside reflective a* value, at a normal viewing angle, of from −3 to +1.
 31. The IG window unit of claim 19, wherein the coating has a sheet resistance (R_(s)) of no greater than 3.0 ohms/square.
 32. The IG window unit of claim 19, wherein the glass substrate supporting the coating is not heat treated with the coating thereon.
 33. The IG window unit of claim 19, wherein the IG unit has an outside a* value which does not change by more than 3.5 given a viewing angle shift from 0 to 45 degrees.
 34. The IG window unit of claim 19, wherein the IG unit has an outside a* value which does not change by more than 2.5 given a viewing angle shift from 0 to 45 degrees.
 35. The IG window unit of claim 19, wherein outside reflective a* and b* of the IG window unit do not change by more than 3.5 given a viewing angle shift from 0 to 45 degrees.
 36. An insulating glass (IG) window unit comprising: first and second glass substrates, and a coating supported by one of the substrates, the coating comprising first and second infrared (IR) reflecting layers comprising silver, with no other IR reflecting layer(s) comprising silver being provided in the coating; and wherein the IG window unit has a selectivity (T_(vis)/SF) of at least 1.75, and a solar factor (SF) of no greater than
 34. 37. The IG window unit of claim 36, wherein the IG window unit has a selectivity of at least 1.80, and wherein the IG window unit has a visible transmission of from 50 to 760%.
 38. The IG window unit of claim 1, wherein the first and second contact layers each comprise an oxide of the same metal(s).
 39. The IG window unit of claim 19, wherein the IR reflecting layers comprise silver, and wherein the contact layer under at least one of the layers comprising silver is oxided to a lesser extent than is the contact layer located over and contacting that layer comprising silver, and wherein each of the contact layers contacting that layer comprising silver comprise an oxide of the same metal(s).
 40. A coated article including a coating supported by a glass substrate, the coating comprising: at least one layer comprising silver sandwiched between and contacting first and second oxided contact layers, wherein the first contact layer is located below said layer comprising silver and is oxided to a lesser extent than is the second contact layer located above said layer comprising silver; and wherein the coated article has a selectivity (T_(vis)/SF) of at least 1.75.
 41. The coated article of claim 40, wherein the article has a selectivity of at least 1.80.
 42. The coated article of claim 40, wherein the article has a selectivity of at least 1.85.
 43. A method of making a coated article having only two IR reflecting layers comprising silver, the method comprising: a) providing a glass substrate; b) forming a first IR reflecting layer comprising silver; c) forming a first contact layer comprising an oxide of at least one metal; d) forming a second IR reflecting layer comprising silver on and in contact with the first contact layer; e) forming a second contact layer comprising an oxide of at least one metal on and in contact with the second IR reflecting layer comprising silver; and f) wherein steps c) and e) are performed so that the first contact layer is deposited in a manner so as to be less oxided than the second contact layer as deposited and so that the resulting coated article has a selectivity of at least 1.75.
 44. The method of claim 43, wherein each of said forming steps comprises sputtering at least one target.
 45. The method of claim 43, wherein steps c) and e) are performed so that the resulting coated article has a selectivity of at least 1.80.
 46. The method of claim 43, wherein steps c) and e) are performed so that the resulting coated article has a selectivity of at least 1.85.
 47. The method of claim 43, wherein steps c) and e) are performed so that the resulting coated article has a SF of no greater than 33.0.
 48. The IG window unit of claim 1, wherein reflective/outside color of the IG window unit does not significantly change as a function of polarization state of incident light.
 49. The IG window unit of claim 19, wherein reflective/outside color of the IG window unit does not significantly change as a function of polarization state of incident light. 